Thermal Property and Thermodynamic Parameter of Rubber Blends Containing the Cyclic Structure

Erschienen in: KGK - Kautschuk Gummi Kunststoffe - 04/2009

Autor: S. Riyajan, Hat Yai (Thailand), J. T. Sakdapipanich, Bangkok (Thailand)

Natural rubber (NR) and cyclized NR (90 % cyclization) were blended by dynamic vulcanization using a sulfur curing systems. The rate of vulcanization was slower in rubber blends containing cyclized NR was slower than the one of pure NR. Activation energies have been determined and the order of the thermal oxidative stability evaluated. It was seen that the activation energy of NR phase and the cyclized NR phase was 330-357 kJ/mole and 810- 905 kJ/mole, respectively. Moreover, the enthalpy of activation of all sample (with or without cyclized NR) decreased with increasing of frequency.

Thermische Eigenschaften und thermodynamische Parameter von Verschnitten aus Kautschuken mit cyklischen Strukturen.
Narturkautschuk (NR) und zyklisierter NR (90 % Zyklengehalt) wurden mit Hilfe eines Schwefelsystems dynamisch vulkanisiert. Die Vulkanisationsgeschwindigkeit des zyklisierten NR ist geringer als die von einem NR. Die Aktivierungsenergien wurden ermittelt und die thermisch-oxidative Stabilität bewertet. Es wurde gezeigt, dass die Aktivierungsenergie der NR-Phase 330- 357 kJ/mol bzw. die der zyklisierte NR Phase 810-905 kJ/mol betragen. Darüber hinaus nimmt die Aktivierungsenthalpie bei den Phasen mit zunehmender Frequenz ab.

Dieser Artikel ist in englisch.

Download (PDF - 454 kB)