1H-NMR Relaxation Study of Cross-Linking and Aging Processes in Polyurethane Coatings

Erschienen in: KGK - Kautschuk Gummi Kunststoffe - 05/2006

Autor: M. Fratricova, P. Schwarzer, Wolfsburg, W. Kuhn, Blieskastel

1H-NMR transversal relaxation measurements have been successfully applied for determination of T2 in three types of model polyurethane coatings. The emphasis was given on the comparison of the cross-linking state before and after artificial exposure. Temperature dependence of T2 for differently cross-linked polyester-polyurethane systems has also been measured. Results show a clear dependence of NMR parameters on polyurethane cross-linking and aging. Additionally, industrial coatings at five different grades of crosslinking have been examined.

Untersuchung des Einflusses von oxidativen Alterungsprozessen und dem Effekt von Lichtschutz-Stabilisatoren auf die Vernetzungsdichte von Polyurethan-Lacken mittels 1H-NMR Relaxationszeit-Messungen
Transversale 1H-NMR Relaxationsuntersuchungen wurden erfolgreich zur Charakterisierung der Vernetzungsdichte von Alterungsprozessen an drei unterschiedlichen Typen von Polyurethan-Lacken eingesetzt. Der Schwerpunkt der Untersuchungen liegt dabei auf dem Vergleich des Vernetzungszustandes vor und nach der Exposition der Proben bei unterschiedlichen klimatischen Bedingungen. Die Abhängigkeit der T2-Zeiten von der Meßtemperatur und den Alterungsfaktoren wurde ebenfalls untersucht. Die Ergebnisse zeigen eine eindeutige Abhängigkeit der NMR-Parameter von der PUR-Behandlung und den Alterungsbedingungen sowie deren Eignung zur Charakterisierung der Vernetzungsdichte.

Dieser Artikel ist in englisch.

Download (PDF - 229 kB)

FIRMA		Links
IIC Innovative Imaging Corp. KG: Weitere Infos Kontakt aufnehmen		Institutionen, allgemein Weitere Artikel (38) Weitere Produktberichte (23) Weitere Firmen (102)