Investigations of SBR/CSM Blends Reinforced by Carbon Black

Erschienen in: KGK - Kautschuk Gummi Kunststoffe - 05/2006

Autor: G. Markovic, B. Radovanovic, M. Marinovic-Cincovic, J. Budinski-Simendic, Pirot (Serbia and Montenegro)

Blends based on functionally active rubbers are reported to be more compatible due to crosslinking reactions by the functional groups. SBR/CSM blends with different blend ratio were reinforced by carbon black with primary particle sizes of 20–25 nm and 60 nm respectively. In the corresponding compounds the chlorinated polyethylene rubber acts as a chlorine donor (functionally active rubber). The effects of rubber blend ratio and carbon black content on the curing characteristic and mechanical properties were investigated.

Untersuchung von rußverstärkten SBR/CSM Verschnitten
Verschnitte basierend auf funktional aktiven Kautschuken haben eine höhere Verträglichkeit durch zusätzliche Beiträge der funktionalen Gruppen zur Vernetzungsreaktion. Verschiedene SBR/CSM Verschnitte wurden durch Ruße mit Primärteilchengröße von 20–25 nm bzw. 60 nm verstärkt. In den entsprechenden Compounds dienten allylische Chloratome als funktionell aktive Gruppen. Die Effekte des Verhältnisses und des Rußgehaltes wurden hinsichtlich des Vernetzungsverhaltens sowie der mechanischen Eigenschaften untersucht.

Dieser Artikel ist in englisch.

Download (PDF - 305 kB)